Adhesive Film for tempered Glass,

Adhesive Film for Glass
1. Z1261 Fast cure (UV Cutoff) 2. Z1261A High transmission (UV Through)
Item code	Specification of thickness(mm)	Specification of width (mm)	Grammage (g/sqm)	Length/roll (m)	Package means (mm)	Min order quantity （sqm)
Z1261/Z1261A	0.38	300-2200	300-350	120-150	-	3,000
	0.50	300-2200	400-450	100-130	-	3,000
	0.76	300-2200	580-630	60-90	-	10,000
	other customize	200-2200	-	-	-	10,000

Product Packaging :

1.Each roll is packed with PE film and vacuum packing process, after that put one roll in one carbon box.
2.The inner package materials are polyethylene bag or protect paper, and the external packages are carton boxes and pallets, and each pallet can be put on 9 to 18 rolls.
3.Production storage: Being stored in a dry and shade place with temperature 0℃～30℃, and humidity ≤ 60%, sunlight direct radiation should be avoided. The product must be not placed nearby heating equipment and the place with dust.
4.Product usage: Before using, check the package intact and untouched. The product should be quickly used once you open it. The other unused part re-sealed by original packaging or similar packaging. The product is guaranteed for 6 months from the production date in the unopened state, you are suggested to use up within 3 months.

Item		Test method	Unit	EVA Film for Glass
Item		Test method	Unit			Z1261A UV thtough	Z1261 UV Cutoff
Density		ISO1183	g/cm³	0.95	0.95
VA content		TGA	％	26-33	26-33
Softening point		DSC	℃	55	55
Surface hardness		GB/T531-1999	Shore A	65	65
Tensile strenghth (after crosslinking)		ISO527-3	MPa	20	20
Elongation (after crosslinking)			%	600	600
Strenghth of Extension			MPa	6	6
UV cutoff wavelength		UV-vis	Nm	--	360
Optical transmission		GB2410-80	%	91.5	91
Refractive index		ISO489	--	1.480	1.482
Thermal shrinkage（0.45MM: before test, 120℃, 3min）		Q/ZX001-2012	MD%	≤3.0	≤3.0
Thermal shrinkage（0.45MM: before test, 120℃, 3min）		Q/ZX001-2012	TD%	≤1.0	≤1.0
Cross-linking rate (140℃,17min)		Q/ZX001-2012	Gel %	≥75.0
Peeling strength	With Glass	Q/ZX001-2012	N/cm	>60
Peeling strength	With TPT	Q/ZX001-2012	N/cm	>40
Damp Heat resistance test (90℃,90%RH, 1500hrs)	Yellowness index	Q/ZX001-2012	△YI	<3
Damp Heat resistance test (90℃,90%RH, 1500hrs)	Peeling strenghth with glass	Q/ZX001-2012	N/cm	＞40
UV Exposure Resistance (Xenon lamp ，1500hrs)	Yellowness index	Q/ZX001-2012	△YI	<3
UV Exposure Resistance (Xenon lamp ，1500hrs)	Peeling strenghth with glass	Q/ZX001-2012	N/cm	＞40
Volume resistance		GB/T 1410	Ω·cm	≥1*1015
Dielectric strength		GB/T1408.1	Kv/mm	＞28
PID resistance test (85℃,85%RH,-1000V,96H)		IEC61730-2:2004 IEC61215:2005	Power loss %	<5%

Operating Items		Adhesive Film For Glass
		Z1261 / Z1261A
Laminating curing parameters	Heating panel (℃)	135±2	140±2	145±2	150±2


	Pump down time (min)	5±1	5±1	4±1	4±1
	Holding time(min)	15±2	12±1	10±1	7±1

Note: Laminating process conditions shall be selected and confirmed according to the performance of laminating machine.